Visible luminescence properties of Er³⁺-Dy³⁺ codoped tellurite glasses

Er³⁺ and Dy³⁺ codoped tellurite glasses have been synthesized. Five emission bands in the PL spectrum under 325 nm pumping were observed. Three of them correspond to Er³⁺ and the other two correspond to Dy³⁺, respectively. The PL spectrum revealed that the intensity of Dy³⁺ characteristic emission was enhanced as Er ³⁺ concentration increased while keeping Dy³⁺ concentration constant. Due to small mismatch between the energy level of Er³⁺:⁴F_7/2 and Dy³⁺: ⁴F_9/2 resonant energy was possibly transferred between them. This process can give rise to an enhancement of the PL intensity of 484 and 574 nm from Dy³⁺. The PL spectra of these glasses cover the blue, green and red wavelength range and the intensities of those emission bands could be controlled by adjusting the concentration of relevant rare-earth ions. These glasses with the controllable CIE coordinates might be a potential candidate for the widely realistic application such as solid-state white lighting and multicolor display.