Thermo-physical and mechanical properties of Yb₂O₃ and Sc₂O₃ co-doped Gd₂Zr₂O₇ ceramics

Ceramic materials for the thermal barrier coating (TBC) application of Gd₂Zr₂O₇ (GZO), (Gd_0.94Yb_0.06)₂Zr₂O₇ (GYb_0.06Z), (Gd_0.925Sc_0.075)₂Zr₂O₇ (GSc_0.075Z), (Gd_0.865Sc_0.075Yb_0.06)₂Zr₂O₇ (GSc_0.075Yb_0.06Z), and (Gd_0.8Sc_0.1Yb_0.1)₂Zr₂O₇ (GSc_0.1Yb_0.1Z) were successfully synthesized by chemical co-precipitation. The effects of the doping of Sc₂O₃ and Yb₂O₃ on the phases, thermo-physical and mechanical properties of the ceramics were investigated. The results show that both Yb₂O₃ and Sc₂O₃ doping promoted the phase transition of GZO from pyrochlore to fluorite. All the Sc₂O₃-doped samples exhibited enhanced fracture toughness, as compared to the undoped sample. Furthermore, the GSc_0.075Yb_0.06Z sample revealed a thermal conductivity of ~0.8 W/mK at 1200 °C, which was nearly 30% lower than that of the undoped sample. The associated mechanisms related to the effects of the doping on the thermophysical and mechanical properties are discussed.