The influence of Gd doping on thermophysical properties, elasticity modulus and phase stability of garnet-type (Y_1-xGd_x)₃Al₅O₁₂ ceramics

In this work, Gd³⁺ was selected to partially substitute the Y³⁺ in yttrium aluminum garnet (YAG) in order to improve the thermophysical properties of YAG. A series of (Y_1-xGd_x)₃Al₅O₁₂ (x = 0, 0.1, 0.2, 0.3, 0.4) ceramics were synthesized through chemical co-precipitation route. The microstructure, thermophysical properties and elasticity modulus of (Y_1-xGd_x)₃Al₅O₁₂ were investigated. The (Y_1-xGd_x)₃Al₅O₁₂ ceramics was comprised of single garnet-type Y₃Al₅O₁₂ phase. The thermal conductivities of (Y_1-xGd_x)₃Al₅O₁₂ bulk samples decreased with increasing doping concentration to 0.2, but increased with furthering increasing the concentration to 0.4. The thermal conductivity of (Y_0.8Gd_0.2)₃Al₅O₁₂ was 1.51 W m⁻¹ K⁻¹ at 1200 °C. The average thermal expansion coefficient of (Y_0.8Gd_0.2)₃Al₅O₁₂ was slightly larger than that of Y₃Al₅O₁₂. (Y_0.8Gd_0.2)₃Al₅O₁₂ bulk sample exhibited the lowest elasticity modulus among the investigated (Y_1-xGd_x)₃Al₅O₁₂. In addition, (Y_0.8Gd_0.2)₃Al₅O₁₂ ceramic remained good phase stability from room temperature to 1600 °C.