TY - JOUR
T1 - The effect of scandium addition on microstructure and mechanical properties of Al-Si-Mg alloy
T2 - A multi-refinement modifier
AU - Xu, Cong
AU - Xiao, Wenlong
AU - Hanada, Shuji
AU - Yamagata, Hiroshi
AU - Ma, Chaoli
N1 - Publisher Copyright:
© 2015 Elsevier Inc.
PY - 2015/12/1
Y1 - 2015/12/1
N2 - Effect of scandium (Sc) additions on the microstructure, mechanical properties and fracture behavior of Al-Si-Mg casting alloy (F357) were systematically investigated. It was found that Sc addition caused a multi-refining efficiency on the microstructure of as-cast F357 alloy, including refinement of grains and secondary dendrite arm spacing (SDAS), modification of eutectic Si and harmless disposal of β-Al5FeSi phase. Subsequent T6 heat treatment had further induced the complete spheroidization of eutectic Si and precipitation of fine secondary Al3Sc dispersoids in the Sc modified alloys. Thus the mechanical properties, especially the ductility, were significantly enhanced by the addition of Sc combined with the heat treatment. The highest ultimate tensile strength, yield strength and elongation were achieved in 0.8 wt.% Sc modified F357 alloy combined with T6 heat treatment. Furthermore, fractographic examinations indicated that the ductile fracture mechanism served as a dominate role in the modified alloys due to the formation of fine, deep and uniformly distributed dimples.
AB - Effect of scandium (Sc) additions on the microstructure, mechanical properties and fracture behavior of Al-Si-Mg casting alloy (F357) were systematically investigated. It was found that Sc addition caused a multi-refining efficiency on the microstructure of as-cast F357 alloy, including refinement of grains and secondary dendrite arm spacing (SDAS), modification of eutectic Si and harmless disposal of β-Al5FeSi phase. Subsequent T6 heat treatment had further induced the complete spheroidization of eutectic Si and precipitation of fine secondary Al3Sc dispersoids in the Sc modified alloys. Thus the mechanical properties, especially the ductility, were significantly enhanced by the addition of Sc combined with the heat treatment. The highest ultimate tensile strength, yield strength and elongation were achieved in 0.8 wt.% Sc modified F357 alloy combined with T6 heat treatment. Furthermore, fractographic examinations indicated that the ductile fracture mechanism served as a dominate role in the modified alloys due to the formation of fine, deep and uniformly distributed dimples.
KW - Fracture
KW - Mechanical properties
KW - Microstructure
KW - Multi-refining efficiency
KW - Scandium
UR - https://www.scopus.com/pages/publications/84945917304
U2 - 10.1016/j.matchar.2015.10.030
DO - 10.1016/j.matchar.2015.10.030
M3 - 文章
AN - SCOPUS:84945917304
SN - 1044-5803
VL - 110
SP - 160
EP - 169
JO - Materials Characterization