摘要

Mesoporous TiO₂ with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO₂ had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m² g^-1 after calcinating at 450 °C.

源语言	英语
页（从-至）	1-3
页数	3
期刊	Journal of Sol-Gel Science and Technology
卷	51
期	1
DOI	https://doi.org/10.1007/s10971-009-1984-4
出版状态	已出版 - 7月 2009
已对外发布	是

访问文件

10.1007/s10971-009-1984-4

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{a0ee83fe9b36401f9aa6f5e3350311d9,

title = "Simple sol-gel route to synthesis of mesoporous TiO2",

abstract = "Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.",

keywords = "Formamide, Mesoporous TiO, Sol-gel, Titanium sulfate",

author = "Xin Zhang and Xiaogang Li and Junsheng Wu and Renchun Yang and Limin Tian and Zhihua Zhang",

year = "2009",

month = jul,

doi = "10.1007/s10971-009-1984-4",

language = "英语",

volume = "51",

pages = "1--3",

journal = "Journal of Sol-Gel Science and Technology",

issn = "0928-0707",

publisher = "Springer Netherlands",

number = "1",

}

TY - JOUR

T1 - Simple sol-gel route to synthesis of mesoporous TiO2

AU - Zhang, Xin

AU - Li, Xiaogang

AU - Wu, Junsheng

AU - Yang, Renchun

AU - Tian, Limin

AU - Zhang, Zhihua

PY - 2009/7

Y1 - 2009/7

N2 - Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.

AB - Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.

KW - Formamide

KW - Mesoporous TiO

KW - Sol-gel

KW - Titanium sulfate

UR - https://www.scopus.com/pages/publications/65649120034

U2 - 10.1007/s10971-009-1984-4

DO - 10.1007/s10971-009-1984-4

M3 - 文章

AN - SCOPUS:65649120034

SN - 0928-0707

VL - 51

SP - 1

EP - 3

JO - Journal of Sol-Gel Science and Technology

JF - Journal of Sol-Gel Science and Technology

IS - 1

ER -

Simple sol-gel route to synthesis of mesoporous TiO2

摘要

访问文件

其它文件与链接

指纹

引用此

Simple sol-gel route to synthesis of mesoporous TiO₂