Removal analyses of chip and rod in rotary ultrasonic-assisted drilling of carbon fiber-reinforced plastics using core drill

Carbon fiber-reinforced plastics (CFRP) have been widely applied in aerospace industry as structural components due to their excellent mechanical and physical properties. Meanwhile, the drilling process is indispensable for machining the assembly holes of CFRP. However, in the conventional drilling process of CFRP, it is prone to produce the defects including delamination, spalling, fuzzing, and tool wear. In recent years, the rotary ultrasonic-assisted drilling (RUAD) with diamond core drill, as a novel machining method, has been employed to reduce the defects. But this is few reported investigations on chip adhesion of tool surface and machined rod jamming into core drill tool during RUAD of CFRP. Therefore, this paper detailedly reported a study on removal analyses of chip and rod in RUAD of CFRP using core drill under no cooling condition for the first time. To begin with, the principle analysis on RUAD of CFRP was presented to illustrate the removal process of chip and rod. And then, the experiment analysis on RUAD of CFRP was carried out to observe the removal effects of chip and rod. The experimental results indicated that compared with the common drilling of core drill, when the vibration amplitude reached 5.0 and 7.5 μm in RUAD, the cutting ability of core drill tool was greatly enhanced, excellent removal effects of chip and rod were obtained, which obviously reduced the chip adhesion, rod jamming, rod fragmentation, thrust force, cutting temperature, and surface roughness, improved the dimensional accuracy of machined hole and rod diameter, prolonged the tool life, as well as acquired superior surface integrity of machined hole and flat fibers fracture surfaces. Furthermore, the experimental results also validated the accuracy of the principle analysis.