Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La0.67Ba0.33MnO3 compound by hydrogen annealing

Yimin Cui; Liuwan Zhang; Rongming Wang

doi:10.1016/j.jallcom.2006.03.058

Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La_0.67Ba_0.33MnO₃ compound by hydrogen annealing

Yimin Cui^*
, Liuwan Zhang
, Rongming Wang

^*此作品的通讯作者

物理学院

Tsinghua University
Beihang University

科研成果: 期刊稿件 › 文章 › 同行评审

4 引用（Scopus）

摘要

Anomalous annealing behaviors of insulator-metal transition temperature (T_P) and ac magnetic susceptibility were investigated in different prepared polycrystalline La_0.67Ba_0.33MnO₃ bulk samples which were annealed in a flow of 95%Ar:5%H₂(AH) at 700 °C for different time, and the behaviors were effects of oxygen loss and Ba ion vacancies. The experiments indicated that different prepared samples had different speed of oxygen loss and Ba ion vacancies during AH annealing. Different prepared samples had different content of structure defects, especially for the quenching samples, in which there were high stress and high defect content, the speed of oxygen loss and Ba²⁺ vacancies were the fastest during AH annealing, that was to say that quenching promote the hydrogen annealing effects on polycrystalline La_0.67Ba_0.33MnO₃ compound.

源语言	英语
页（从-至）	40-43
页数	4
期刊	Journal of Alloys and Compounds
卷	428
期	1-2
DOI	https://doi.org/10.1016/j.jallcom.2006.03.058
出版状态	已出版 - 31 1月 2007

访问文件

10.1016/j.jallcom.2006.03.058

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{c49d5fd0ecf141b58f65622f22755338,

title = "Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La0.67Ba0.33MnO3 compound by hydrogen annealing",

abstract = "Anomalous annealing behaviors of insulator-metal transition temperature (TP) and ac magnetic susceptibility were investigated in different prepared polycrystalline La0.67Ba0.33MnO3 bulk samples which were annealed in a flow of 95\%Ar:5\%H2(AH) at 700 °C for different time, and the behaviors were effects of oxygen loss and Ba ion vacancies. The experiments indicated that different prepared samples had different speed of oxygen loss and Ba ion vacancies during AH annealing. Different prepared samples had different content of structure defects, especially for the quenching samples, in which there were high stress and high defect content, the speed of oxygen loss and Ba2+ vacancies were the fastest during AH annealing, that was to say that quenching promote the hydrogen annealing effects on polycrystalline La0.67Ba0.33MnO3 compound.",

keywords = "Defect and oxygen content, Hydrogen annealing, Manganite",

author = "Yimin Cui and Liuwan Zhang and Rongming Wang",

year = "2007",

month = jan,

day = "31",

doi = "10.1016/j.jallcom.2006.03.058",

language = "英语",

volume = "428",

pages = "40--43",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

number = "1-2",

}

TY - JOUR

T1 - Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La0.67Ba0.33MnO3 compound by hydrogen annealing

AU - Cui, Yimin

AU - Zhang, Liuwan

AU - Wang, Rongming

PY - 2007/1/31

Y1 - 2007/1/31

N2 - Anomalous annealing behaviors of insulator-metal transition temperature (TP) and ac magnetic susceptibility were investigated in different prepared polycrystalline La0.67Ba0.33MnO3 bulk samples which were annealed in a flow of 95%Ar:5%H2(AH) at 700 °C for different time, and the behaviors were effects of oxygen loss and Ba ion vacancies. The experiments indicated that different prepared samples had different speed of oxygen loss and Ba ion vacancies during AH annealing. Different prepared samples had different content of structure defects, especially for the quenching samples, in which there were high stress and high defect content, the speed of oxygen loss and Ba2+ vacancies were the fastest during AH annealing, that was to say that quenching promote the hydrogen annealing effects on polycrystalline La0.67Ba0.33MnO3 compound.

AB - Anomalous annealing behaviors of insulator-metal transition temperature (TP) and ac magnetic susceptibility were investigated in different prepared polycrystalline La0.67Ba0.33MnO3 bulk samples which were annealed in a flow of 95%Ar:5%H2(AH) at 700 °C for different time, and the behaviors were effects of oxygen loss and Ba ion vacancies. The experiments indicated that different prepared samples had different speed of oxygen loss and Ba ion vacancies during AH annealing. Different prepared samples had different content of structure defects, especially for the quenching samples, in which there were high stress and high defect content, the speed of oxygen loss and Ba2+ vacancies were the fastest during AH annealing, that was to say that quenching promote the hydrogen annealing effects on polycrystalline La0.67Ba0.33MnO3 compound.

KW - Defect and oxygen content

KW - Hydrogen annealing

KW - Manganite

UR - https://www.scopus.com/pages/publications/33845685589

U2 - 10.1016/j.jallcom.2006.03.058

DO - 10.1016/j.jallcom.2006.03.058

M3 - 文章

AN - SCOPUS:33845685589

SN - 0925-8388

VL - 428

SP - 40

EP - 43

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

IS - 1-2

ER -

Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La0.67Ba0.33MnO3 compound by hydrogen annealing

摘要

访问文件

其它文件与链接

学术指纹

引用此

Quenching-promoted anomalous electromagnetic behaviors of polycrystalline La_0.67Ba_0.33MnO₃ compound by hydrogen annealing