Novel thermal barrier coatings based on La₂Ce₂O₇/8YSZ double-ceramic-layer systems deposited by electron beam physical vapor deposition

Novel thermal barrier coatings based on La₂Ce₂O₇/8YSZ double-ceramic-layer (DCL) systems, which were deposited by electron beam physical vapor deposition (EB-PVD), were found to have a longer lifetime compared to the single layer La₂Ce₂O₇ (LC) system, and even much longer than that of the single layer 8YSZ system under burner rig test. The DCL coating structure design can effectively alleviate the thermal expansion mismatch between LC coating and bond coat, as well as avoid the chemical reaction between LC and Al₂O₃ in thermally grown oxide (TGO), which occurs above 1000 °C as determined by differential scanning calorimetry (DSC) analysis. The failure mechanism of LC/8YSZ DCL coating is mainly due to the sintering of LC coating surface after long-term thermal cycling.