Non-Preheating Processed Quasi-2D Perovskites for Efficient and Stable Solar Cells

Although the hot-casting (HC) technique is prevalent in developing preferred crystal orientation of quasi-2D perovskite films, the difficulty of accurately controlling the thermal homogeneity of substrate is unfavorable for the reproducibility of device fabrication. Herein, a facile and effective non-preheating (NP) film-casting method is proposed to realize highly oriented quasi-2D perovskite films by replacing the butylammonium (BA⁺) spacer partially with methylammonium (MA⁺) cation as (BA)_{2− x}(MA)_{3+ x}Pb₄I₁₃ (x = 0, 0.2, 0.4, and 0.6). At the optimal x-value of 0.4, the resultant quasi-2D perovskite film possesses highly orientated crystals, associated with a dense morphology and uniform grain-size distribution. Consequently, the (BA)_1.6(MA)_3.4Pb₄I₁₃-based solar cells yield champion efficiencies of 15.44% with NP processing and 16.29% with HC processing, respectively. As expected, the HC-processed device shows a poor performance reproducibility compared with that of the NP film-casting method. Moreover, the unsealed device (x = 0.4) displays a better moisture stability with respect to the x = 0 stored in a 65% ± 5% relative humility chamber.