Microscale lamellar NiCoCrAlY coating with improved oxidation resistance

Hui Peng; Hongbo Guo; Jian He; Shengkai Gong

doi:10.1016/j.surfcoat.2012.06.034

Microscale lamellar NiCoCrAlY coating with improved oxidation resistance

Hui Peng
, Hongbo Guo^*
, Jian He
, Shengkai Gong

^*此作品的通讯作者

材料科学与工程学院

科研成果: 期刊稿件 › 文章 › 同行评审

28 引用（Scopus）

摘要

A novel NiCoCrAlY coating was fabricated by plasma activated electron beam-physical vapor deposition (PA EB-PVD). Within the duplex coating, the β-NiAl phase precipitated as small lamellae (less than 1μm thick) in a γ matrix, predominantly oriented perpendicular to the coating surface. The oxidation results at 1373K show that the scaling rate constant during the steady-state oxidation of the novel coating is reduced by approximately 70% as compared with the conventional coating of similar composition produced by electron beam-physical vapor deposition (EB-PVD). This reduction in oxidation rate is attributed to a slower θ→α Al ₂O ₃ phase transformation during the initial stages of oxidation.

源语言	英语
页（从-至）	110-116
页数	7
期刊	Surface and Coatings Technology
卷	207
DOI	https://doi.org/10.1016/j.surfcoat.2012.06.034
出版状态	已出版 - 25 8月 2012

访问文件

10.1016/j.surfcoat.2012.06.034

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{e04f6a6916724c53808d308f371138d4,

title = "Microscale lamellar NiCoCrAlY coating with improved oxidation resistance",

abstract = "A novel NiCoCrAlY coating was fabricated by plasma activated electron beam-physical vapor deposition (PA EB-PVD). Within the duplex coating, the β-NiAl phase precipitated as small lamellae (less than 1μm thick) in a γ matrix, predominantly oriented perpendicular to the coating surface. The oxidation results at 1373K show that the scaling rate constant during the steady-state oxidation of the novel coating is reduced by approximately 70\% as compared with the conventional coating of similar composition produced by electron beam-physical vapor deposition (EB-PVD). This reduction in oxidation rate is attributed to a slower θ→α Al 2O 3 phase transformation during the initial stages of oxidation.",

keywords = "Alumina scale, Coating, Oxidation, Plasma activated electron beam-physical vapor deposition (PA EB-PVD)",

author = "Hui Peng and Hongbo Guo and Jian He and Shengkai Gong",

year = "2012",

month = aug,

day = "25",

doi = "10.1016/j.surfcoat.2012.06.034",

language = "英语",

volume = "207",

pages = "110--116",

journal = "Surface and Coatings Technology",

issn = "0257-8972",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Microscale lamellar NiCoCrAlY coating with improved oxidation resistance

AU - Peng, Hui

AU - Guo, Hongbo

AU - He, Jian

AU - Gong, Shengkai

PY - 2012/8/25

Y1 - 2012/8/25

N2 - A novel NiCoCrAlY coating was fabricated by plasma activated electron beam-physical vapor deposition (PA EB-PVD). Within the duplex coating, the β-NiAl phase precipitated as small lamellae (less than 1μm thick) in a γ matrix, predominantly oriented perpendicular to the coating surface. The oxidation results at 1373K show that the scaling rate constant during the steady-state oxidation of the novel coating is reduced by approximately 70% as compared with the conventional coating of similar composition produced by electron beam-physical vapor deposition (EB-PVD). This reduction in oxidation rate is attributed to a slower θ→α Al 2O 3 phase transformation during the initial stages of oxidation.

AB - A novel NiCoCrAlY coating was fabricated by plasma activated electron beam-physical vapor deposition (PA EB-PVD). Within the duplex coating, the β-NiAl phase precipitated as small lamellae (less than 1μm thick) in a γ matrix, predominantly oriented perpendicular to the coating surface. The oxidation results at 1373K show that the scaling rate constant during the steady-state oxidation of the novel coating is reduced by approximately 70% as compared with the conventional coating of similar composition produced by electron beam-physical vapor deposition (EB-PVD). This reduction in oxidation rate is attributed to a slower θ→α Al 2O 3 phase transformation during the initial stages of oxidation.

KW - Alumina scale

KW - Coating

KW - Oxidation

KW - Plasma activated electron beam-physical vapor deposition (PA EB-PVD)

UR - https://www.scopus.com/pages/publications/84865803554

U2 - 10.1016/j.surfcoat.2012.06.034

DO - 10.1016/j.surfcoat.2012.06.034

M3 - 文章

AN - SCOPUS:84865803554

SN - 0257-8972

VL - 207

SP - 110

EP - 116

JO - Surface and Coatings Technology

JF - Surface and Coatings Technology

ER -

Microscale lamellar NiCoCrAlY coating with improved oxidation resistance

摘要

访问文件

其它文件与链接

学术指纹

引用此