Micelle-assisted strategy for the direct synthesis of large-sized mesoporous platinum catalysts by vapor infiltration of a reducing agent

Stable polymeric micelles have been demonstrated to serve as suitable templates for creating mesoporous metals. Herein, we report the utilization of a core-shell-corona type triblock copolymer of poly(styrene-b-2-vinylpyridine-b-ethylene oxide) and H₂PtCl₆·H₂O to synthesize large-sized mesoporous Pt particles. After formation of micelles with metal ions, the reduction process has been carried out by vapor infiltration of a reducing agent, 4-(Dimethylamino)benzaldehyde. Following the removal of the pore-directing agent under the optimized temperature, mesoporous Pt particles with an average pore size of 15 nm and surface area of 12.6 m²·g⁻¹ are achieved. More importantly, the resulting mesoporous Pt particles exhibit superior electrocatalytic activity compared to commercially available Pt black.