Investigation of TiC-Al2O3-Fe cermet by SHS

Hua Yu Zhang; Jie Cai Han; Wei Fang Zhang; Shan Yi Du

Investigation of TiC-Al₂O₃-Fe cermet by SHS

Hua Yu Zhang^*
, Jie Cai Han
, Wei Fang Zhang
, Shan Yi Du

^*此作品的通讯作者

Harbin Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

Densified TiC-Al₂O₃-20Fe cermet was produced by self-propagating high temperature synthesis and pseudo-hot isostatic pressing (SHS/PHIP). The composition, microstructure and properties of the product were analyzed- The results show that the cermet consists of TiC and A1 ₂O₃ particles and quasi-continuous Fe-binder phase. The interfacial bonding between Fe and A1₂O₃ is smooth. Transverse rupture strength and compressive strength are approximately 890MPa and 18. 4GPa.

源语言	英语
页（从-至）	23-26
页数	4
期刊	Journal of Materials Engineering
期	5
出版状态	已出版 - 1999
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{73ecf5bffbab4e25b89c3f44835dd310,

title = "Investigation of TiC-Al2O3-Fe cermet by SHS",

abstract = "Densified TiC-Al2O3-20Fe cermet was produced by self-propagating high temperature synthesis and pseudo-hot isostatic pressing (SHS/PHIP). The composition, microstructure and properties of the product were analyzed- The results show that the cermet consists of TiC and A1 2O3 particles and quasi-continuous Fe-binder phase. The interfacial bonding between Fe and A12O3 is smooth. Transverse rupture strength and compressive strength are approximately 890MPa and 18. 4GPa.",

keywords = "Fe binder, SHS/PHIP, TiC-AlO-Fe cermet",

author = "Zhang, \{Hua Yu\} and Han, \{Jie Cai\} and Zhang, \{Wei Fang\} and Du, \{Shan Yi\}",

year = "1999",

language = "英语",

pages = "23--26",

journal = "Journal of Materials Engineering",

issn = "1001-4381",

publisher = "Science Press ",

number = "5",

}

TY - JOUR

T1 - Investigation of TiC-Al2O3-Fe cermet by SHS

AU - Zhang, Hua Yu

AU - Han, Jie Cai

AU - Zhang, Wei Fang

AU - Du, Shan Yi

PY - 1999

Y1 - 1999

N2 - Densified TiC-Al2O3-20Fe cermet was produced by self-propagating high temperature synthesis and pseudo-hot isostatic pressing (SHS/PHIP). The composition, microstructure and properties of the product were analyzed- The results show that the cermet consists of TiC and A1 2O3 particles and quasi-continuous Fe-binder phase. The interfacial bonding between Fe and A12O3 is smooth. Transverse rupture strength and compressive strength are approximately 890MPa and 18. 4GPa.

AB - Densified TiC-Al2O3-20Fe cermet was produced by self-propagating high temperature synthesis and pseudo-hot isostatic pressing (SHS/PHIP). The composition, microstructure and properties of the product were analyzed- The results show that the cermet consists of TiC and A1 2O3 particles and quasi-continuous Fe-binder phase. The interfacial bonding between Fe and A12O3 is smooth. Transverse rupture strength and compressive strength are approximately 890MPa and 18. 4GPa.

KW - Fe binder

KW - SHS/PHIP

KW - TiC-AlO-Fe cermet

UR - https://www.scopus.com/pages/publications/71149106084

M3 - 文章

AN - SCOPUS:71149106084

SN - 1001-4381

SP - 23

EP - 26

JO - Journal of Materials Engineering

JF - Journal of Materials Engineering

IS - 5

ER -

Investigation of TiC-Al2O3-Fe cermet by SHS

摘要

其它文件与链接

学术指纹

引用此

Investigation of TiC-Al₂O₃-Fe cermet by SHS