Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater

Yue Pan; Baozhuang Sun; Zhiyong Liu; Wei Wu; Xiaogang Li

doi:10.1016/j.corsci.2022.110640

Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater

Yue Pan
, Baozhuang Sun
, Zhiyong Liu^*
, Wei Wu
, Xiaogang Li

^*此作品的通讯作者

University of Science and Technology Beijing
National Materials Corrosion and Protection Data Center

科研成果: 期刊稿件 › 文章 › 同行评审

67 引用（Scopus）

摘要

In this work, hydrogen effects on passivation and stress corrosion cracking (SCC) of 2205 duplex stainless steel (DSS) in acidified seawater were investigated. Results show hydrogen deteriorates passive film, accelerates localized anodic dissolution (AD) and causes hydrogen damage, leading to high SCC susceptibility by hydrogen embrittlement (HE) and hydrogen facilitated anodic dissolution (HFAD). SCC initiates in ferrite, and propagates as transgranular-SCC (TGSCC) and intergranular-SCC (IGSCC). When loaded along rolling direction (RD), hydrogen segregating in austenite hardens austenite during SCC propagation; while hydrogen enriching in ferrite causes hydrogen enhanced localized plasticity (HELP) effect for transverse direction (TD) load.

源语言	英语
期刊论文编号	110640
期刊	Corrosion Science
卷	208
DOI	https://doi.org/10.1016/j.corsci.2022.110640
出版状态	已出版 - 11月 2022
已对外发布	是

访问文件

10.1016/j.corsci.2022.110640

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{d8717e9b3af34375a80e7bb41ecc5d9e,

title = "Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater",

abstract = "In this work, hydrogen effects on passivation and stress corrosion cracking (SCC) of 2205 duplex stainless steel (DSS) in acidified seawater were investigated. Results show hydrogen deteriorates passive film, accelerates localized anodic dissolution (AD) and causes hydrogen damage, leading to high SCC susceptibility by hydrogen embrittlement (HE) and hydrogen facilitated anodic dissolution (HFAD). SCC initiates in ferrite, and propagates as transgranular-SCC (TGSCC) and intergranular-SCC (IGSCC). When loaded along rolling direction (RD), hydrogen segregating in austenite hardens austenite during SCC propagation; while hydrogen enriching in ferrite causes hydrogen enhanced localized plasticity (HELP) effect for transverse direction (TD) load.",

keywords = "2205 DSS, Hydrogen charging, Hydrogen embrittlement, Passive film, SCC",

author = "Yue Pan and Baozhuang Sun and Zhiyong Liu and Wei Wu and Xiaogang Li",

note = "Publisher Copyright: {\textcopyright} 2022",

year = "2022",

month = nov,

doi = "10.1016/j.corsci.2022.110640",

language = "英语",

volume = "208",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater

AU - Pan, Yue

AU - Sun, Baozhuang

AU - Liu, Zhiyong

AU - Wu, Wei

AU - Li, Xiaogang

PY - 2022/11

Y1 - 2022/11

N2 - In this work, hydrogen effects on passivation and stress corrosion cracking (SCC) of 2205 duplex stainless steel (DSS) in acidified seawater were investigated. Results show hydrogen deteriorates passive film, accelerates localized anodic dissolution (AD) and causes hydrogen damage, leading to high SCC susceptibility by hydrogen embrittlement (HE) and hydrogen facilitated anodic dissolution (HFAD). SCC initiates in ferrite, and propagates as transgranular-SCC (TGSCC) and intergranular-SCC (IGSCC). When loaded along rolling direction (RD), hydrogen segregating in austenite hardens austenite during SCC propagation; while hydrogen enriching in ferrite causes hydrogen enhanced localized plasticity (HELP) effect for transverse direction (TD) load.

AB - In this work, hydrogen effects on passivation and stress corrosion cracking (SCC) of 2205 duplex stainless steel (DSS) in acidified seawater were investigated. Results show hydrogen deteriorates passive film, accelerates localized anodic dissolution (AD) and causes hydrogen damage, leading to high SCC susceptibility by hydrogen embrittlement (HE) and hydrogen facilitated anodic dissolution (HFAD). SCC initiates in ferrite, and propagates as transgranular-SCC (TGSCC) and intergranular-SCC (IGSCC). When loaded along rolling direction (RD), hydrogen segregating in austenite hardens austenite during SCC propagation; while hydrogen enriching in ferrite causes hydrogen enhanced localized plasticity (HELP) effect for transverse direction (TD) load.

KW - 2205 DSS

KW - Hydrogen charging

KW - Hydrogen embrittlement

KW - Passive film

KW - SCC

UR - https://www.scopus.com/pages/publications/85137686351

U2 - 10.1016/j.corsci.2022.110640

DO - 10.1016/j.corsci.2022.110640

M3 - 文章

AN - SCOPUS:85137686351

SN - 0010-938X

VL - 208

JO - Corrosion Science

JF - Corrosion Science

M1 - 110640

ER -

Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater

摘要

访问文件

其它文件与链接

学术指纹

引用此