Ti-45Al-7Nb alloys are produced by liquid-metalcooling (LMC) directional solidification (DS) furnace with different temperature gradients (G) at a range of 40-80 K/cm. The growth directions of primary β phases and the deflection angles relative to the «100»β direction were investigated. The solidification pathway of alloy is: Liq. → Liq. + β → β → β + α → α + γ → lamella (α2 + γ) + B2. Primary dendrite arm spacing δ reduced from 611.4 μm to 508.7 μm when G increased from 40 K cm -1 to 80 K cm-1. Grains with lamellar orientation aligned at the angles of 12-15° and 55° to growth direction were favored for various G. The orientations of the γ lamellas in steady-state regions were identified by the electron backscattered diffraction analysis (EBSD). The results indicated that the growth directions of primary bcc-β dendrites were «211»β and «110»β at 40 K/cm, «210»β and «211» β at 50 K/cm and «211»β at 80 K/cm, the deflection angle of «211»β relative to «100»β direction is 35.3°.
| 源语言 | 英语 |
|---|---|
| 页(从-至) | 69-75 |
| 页数 | 7 |
| 期刊 | High Temperature Materials and Processes |
| 卷 | 32 |
| 期 | 1 |
| DOI | |
| 出版状态 | 已出版 - 2月 2013 |
指纹
探究 'Growth directions of primary phases in directionally solidified Ti-45Al-7Nb alloys' 的科研主题。它们共同构成独一无二的指纹。引用此
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver