TY - JOUR
T1 - Glass formation, corrosion behavior, and mechanical properties of novel Cr-rich Cr-Fe-Mo-C-B-Y bulk metallic glasses
AU - Xu, Tao
AU - Pang, Shujie
AU - Zhang, Tao
N1 - Publisher Copyright:
© 2014 Elsevier B.V. All rights reserved.
PY - 2015/3/15
Y1 - 2015/3/15
N2 - The glass formation, corrosion behavior, and mechanical properties of novel Cr-rich CrxFe58.8-xMo14.7C14.7B9.8Y2 (x = 29.4, 36.75, and 44.1 at.%) bulk metallic glasses (BMGs) were evaluated. It is found that the critical diameter for glass formation and supercooled liquid region remarkably decrease from 3 mm to 1 mm and 68 K to 79 K, respectively, with the increase in Cr content. Compared with SUS316 stainless steel, those BMGs exhibit more excellent corrosion resistance in 1 M HCl solution. However, the corrosion resistance is not significantly improved with increasing Cr content, which may imply that the threshold value of Cr content to efficiently achieve high corrosion resistance for the present alloy system is around 29.4 at.%. In addition, the fracture strength, Vickers microhardness, Young's modulus, shear modulus, and the ratio of hardness to elastic modulus for the present BMGs are up to 4.31 GPa, 14.15 GPa, 249 GPa, 95 GPa, and 0.057, respectively.
AB - The glass formation, corrosion behavior, and mechanical properties of novel Cr-rich CrxFe58.8-xMo14.7C14.7B9.8Y2 (x = 29.4, 36.75, and 44.1 at.%) bulk metallic glasses (BMGs) were evaluated. It is found that the critical diameter for glass formation and supercooled liquid region remarkably decrease from 3 mm to 1 mm and 68 K to 79 K, respectively, with the increase in Cr content. Compared with SUS316 stainless steel, those BMGs exhibit more excellent corrosion resistance in 1 M HCl solution. However, the corrosion resistance is not significantly improved with increasing Cr content, which may imply that the threshold value of Cr content to efficiently achieve high corrosion resistance for the present alloy system is around 29.4 at.%. In addition, the fracture strength, Vickers microhardness, Young's modulus, shear modulus, and the ratio of hardness to elastic modulus for the present BMGs are up to 4.31 GPa, 14.15 GPa, 249 GPa, 95 GPa, and 0.057, respectively.
KW - Bulk metallic glass
KW - Chromium alloy
KW - Corrosion
KW - Elastic properties
KW - Glass-forming ability
KW - Mechanical properties
UR - https://www.scopus.com/pages/publications/84916888633
U2 - 10.1016/j.jallcom.2014.09.166
DO - 10.1016/j.jallcom.2014.09.166
M3 - 文章
AN - SCOPUS:84916888633
SN - 0925-8388
VL - 625
SP - 318
EP - 322
JO - Journal of Alloys and Compounds
JF - Journal of Alloys and Compounds
ER -