title = "Fracture analysis of the tearing NBR aged at different temperature",
abstract = "This paper analyzed the fracture of the tearing NBR 5621 samples under 500mm/min which had been respectively aged for 24 hours at the temperature of -45 °C, 25°C, 70°C and 120°C. It investigated the fracture characteristic of the tearing samples of NBR, which is flat and on it there are some step faceting. The fracture mechanism was also analyzed. The discussion illustrated that the ageing temperature influences the fracture appearance and has little effect on the fracture strength.",
keywords = "Ageing temperature, Fracture mechanism, NBR",
author = "Li Zhao and Shuang Wang and Yu Chen and Weifang Zhang",
year = "2012",
doi = "10.4028/www.scientific.net/AMR.418-420.893",
language = "英语",
isbn = "9783037853269",
series = "Advanced Materials Research",
pages = "893--896",
booktitle = "Materials Processing Technology",
note = "2nd International Conference on Advances in Materials and Manufacturing, ICAMMP 2011 ; Conference date: 16-12-2011 Through 18-12-2011",
}