摘要

The fracture reason of the fractured torsion bar of 50 CrVA was analyzed by fracture surface observation, metallurgical structure observation, hardness test and fatigue strength checking. The result of fatigue strength checking showed that the fracture was mainly caused by higher torsion load. Large-dimension inclusions richly containing Zn in the torsion bar accelerated the crack initiation and shortened fatigue life of the torsion bar.

源语言	英语
页（从-至）	5-7+11
期刊	Journal of Materials Engineering
期	8
出版状态	已出版 - 8月 2010

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{49b56169dc914032aa605f5ccc99a584,

title = "Fracture analysis of 50 CrVA torsion bar",

abstract = "The fracture reason of the fractured torsion bar of 50 CrVA was analyzed by fracture surface observation, metallurgical structure observation, hardness test and fatigue strength checking. The result of fatigue strength checking showed that the fracture was mainly caused by higher torsion load. Large-dimension inclusions richly containing Zn in the torsion bar accelerated the crack initiation and shortened fatigue life of the torsion bar.",

keywords = "50 CrVA, Fatigue fracture, Inclusion, Torsion bar",

author = "Liu, \{Kun Peng\} and You, \{Yi Liang\} and Shan Zhang and Zheng Zhang",

year = "2010",

month = aug,

language = "英语",

pages = "5--7+11",

journal = "Journal of Materials Engineering",

issn = "1001-4381",

publisher = "Science Press ",

number = "8",

}

TY - JOUR

T1 - Fracture analysis of 50 CrVA torsion bar

AU - Liu, Kun Peng

AU - You, Yi Liang

AU - Zhang, Shan

AU - Zhang, Zheng

PY - 2010/8

Y1 - 2010/8

N2 - The fracture reason of the fractured torsion bar of 50 CrVA was analyzed by fracture surface observation, metallurgical structure observation, hardness test and fatigue strength checking. The result of fatigue strength checking showed that the fracture was mainly caused by higher torsion load. Large-dimension inclusions richly containing Zn in the torsion bar accelerated the crack initiation and shortened fatigue life of the torsion bar.

AB - The fracture reason of the fractured torsion bar of 50 CrVA was analyzed by fracture surface observation, metallurgical structure observation, hardness test and fatigue strength checking. The result of fatigue strength checking showed that the fracture was mainly caused by higher torsion load. Large-dimension inclusions richly containing Zn in the torsion bar accelerated the crack initiation and shortened fatigue life of the torsion bar.

KW - 50 CrVA

KW - Fatigue fracture

KW - Inclusion

KW - Torsion bar

UR - https://www.scopus.com/pages/publications/77956388964

M3 - 文章

AN - SCOPUS:77956388964

SN - 1001-4381

SP - 5-7+11

JO - Journal of Materials Engineering

JF - Journal of Materials Engineering

IS - 8

ER -

Fracture analysis of 50 CrVA torsion bar

摘要

其它文件与链接

指纹

引用此