P. Li; L. Zhao; T. M. Qu; X. C. Wang; Z. Han

doi:10.1016/j.physc.2007.02.033

Fabrication and study of thin Bi-2223 round wires

P. Li^*
, L. Zhao
, T. M. Qu
, X. C. Wang
, Z. Han

^*此作品的通讯作者

Tsinghua University

科研成果: 期刊稿件 › 文章 › 同行评审

1 引用（Scopus）

摘要

In this paper, experimental works in fabrication of Bi-2223 round wires are presented. Seven filament Bi-2223 round wires ranging from 1.0 mm to 0.3 mm in diameter were fabricated and studied. The critical current density J_c (77 K, self field) of round wires was of 10³A/cm² order. A correlation between J_c and wire diameter was observed. For round Bi-2223 wires, there is an optimal diameter at which J_c reaches peak value and the value of optimal diameter was found to be related to coarseness of precursor powder.

源语言	英语
页（从-至）	837-840
页数	4
期刊	Physica C: Superconductivity and its Applications
卷	463-465
期	SUPPL.
DOI	https://doi.org/10.1016/j.physc.2007.02.033
出版状态	已出版 - 1 10月 2007
已对外发布	是

访问文件

10.1016/j.physc.2007.02.033

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{421928b1ad914311af8e3925729c7ed6,

title = "Fabrication and study of thin Bi-2223 round wires",

abstract = "In this paper, experimental works in fabrication of Bi-2223 round wires are presented. Seven filament Bi-2223 round wires ranging from 1.0 mm to 0.3 mm in diameter were fabricated and studied. The critical current density Jc (77 K, self field) of round wires was of 103A/cm2 order. A correlation between Jc and wire diameter was observed. For round Bi-2223 wires, there is an optimal diameter at which Jc reaches peak value and the value of optimal diameter was found to be related to coarseness of precursor powder.",

keywords = "Bi-2223, Interface, Outgrowth, Round wires",

author = "P. Li and L. Zhao and Qu, \{T. M.\} and Wang, \{X. C.\} and Z. Han",

year = "2007",

month = oct,

day = "1",

doi = "10.1016/j.physc.2007.02.033",

language = "英语",

volume = "463-465",

pages = "837--840",

journal = "Physica C: Superconductivity and its Applications",

issn = "0921-4534",

publisher = "Elsevier B.V.",

number = "SUPPL.",

}

TY - JOUR

T1 - Fabrication and study of thin Bi-2223 round wires

AU - Li, P.

AU - Zhao, L.

AU - Qu, T. M.

AU - Wang, X. C.

AU - Han, Z.

PY - 2007/10/1

Y1 - 2007/10/1

N2 - In this paper, experimental works in fabrication of Bi-2223 round wires are presented. Seven filament Bi-2223 round wires ranging from 1.0 mm to 0.3 mm in diameter were fabricated and studied. The critical current density Jc (77 K, self field) of round wires was of 103A/cm2 order. A correlation between Jc and wire diameter was observed. For round Bi-2223 wires, there is an optimal diameter at which Jc reaches peak value and the value of optimal diameter was found to be related to coarseness of precursor powder.

AB - In this paper, experimental works in fabrication of Bi-2223 round wires are presented. Seven filament Bi-2223 round wires ranging from 1.0 mm to 0.3 mm in diameter were fabricated and studied. The critical current density Jc (77 K, self field) of round wires was of 103A/cm2 order. A correlation between Jc and wire diameter was observed. For round Bi-2223 wires, there is an optimal diameter at which Jc reaches peak value and the value of optimal diameter was found to be related to coarseness of precursor powder.

KW - Bi-2223

KW - Interface

KW - Outgrowth

KW - Round wires

UR - https://www.scopus.com/pages/publications/34548455465

U2 - 10.1016/j.physc.2007.02.033

DO - 10.1016/j.physc.2007.02.033

M3 - 文章

AN - SCOPUS:34548455465

SN - 0921-4534

VL - 463-465

SP - 837

EP - 840

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

IS - SUPPL.

ER -

Fabrication and study of thin Bi-2223 round wires

摘要

访问文件

其它文件与链接

指纹

引用此