title = "Experimental study on hot bending of 22MnB5 steel",
abstract = "Special V-shaped heat bending test was designed for 22MnB5 hot forming steel of different thicknesses. Blanks after heating 5 min at around 950°C to austenize fully were bended at different temperature conditions, and simultaneously the spring-back behavior and microstructure features of heat bending specimens were investigated. The result shows that 600-650°C temperature zone is optimal for bending forming and martensite texture transforming. Real hot forming anti-collision beams were produced at 600-650°C and comparison bending test was conducted to reveal more qualified mechanics at this temperature zone.",
keywords = "22MnB5, Bending property, Hot forming, Optimal temperature zone, V-shaped test",
author = "Guo, \{R. Q.\} and L. Ying and P. Hu and W. Guo and Han, \{X. Q.\} and Meng, \{Z. H.\}",
year = "2011",
doi = "10.4028/www.scientific.net/AMR.314-316.66",
language = "英语",
isbn = "9783037852156",
series = "Advanced Materials Research",
pages = "66--69",
booktitle = "Advanced Manufacturing Technology",
note = "2011 International Conference on Advanced Design and Manufacturing Engineering, ADME 2011 ; Conference date: 16-09-2011 Through 18-09-2011",
}