TY - JOUR
T1 - Enhanced mechanical properties of epoxy nanocomposites with mildly surface-functionalized graphene oxide by tuned amine species
AU - Fan, Jie
AU - Yang, Jiping
AU - Wang, Letian
AU - Li, Hong
AU - Tian, Junpeng
AU - Ye, Jinrui
AU - Zhao, Yunfeng
N1 - Publisher Copyright:
© 2021 Elsevier B.V.
PY - 2021/8/30
Y1 - 2021/8/30
N2 - The surface functionalization of graphene oxide (GO) is always attractive in modulating the interfacial characteristics, improving the interfacial bonds and mechanical properties of epoxy-based nanocomposites. In this contribution, amine functionalized graphene oxide (AGO) samples were prepared through the surface functionalization of GO using m-xylylenediamine (m-XDA) and polyetheramine D230, respectively. Simultaneously, weakly oxidized and normally oxidized GO samples were both functionalized to obtain AGO samples with low and high amine grafting density. AGO/epoxy nanocomposites were fabricated and their mechanical properties at room temperature (RT) and liquid nitrogen temperature (LNT) were investigated. Interfacial characteristics of the nanocomposites were revealed through experimental and molecular dynamics (MD) simulation methods. It was found that m-XDA grafted GO (MAGO) showed better dispersion in the matrix and prominently higher efficiency in enhancing the mechanical properties of epoxy resin than D230 grafted GO (DAGO). MAGO nanocomposites exhibited tensile strength 18.1% and 11.3% higher than neat epoxy at RT and LNT, respectively. The result was highly consistent with the enhanced interfacial interaction energy between MAGO and epoxy compared to that between DAGO and epoxy as revealed by MD simulation. However, nanocomposites modified by AGO with improved amine grafting density didn't show enhanced mechanical properties as expected from MD simulation.
AB - The surface functionalization of graphene oxide (GO) is always attractive in modulating the interfacial characteristics, improving the interfacial bonds and mechanical properties of epoxy-based nanocomposites. In this contribution, amine functionalized graphene oxide (AGO) samples were prepared through the surface functionalization of GO using m-xylylenediamine (m-XDA) and polyetheramine D230, respectively. Simultaneously, weakly oxidized and normally oxidized GO samples were both functionalized to obtain AGO samples with low and high amine grafting density. AGO/epoxy nanocomposites were fabricated and their mechanical properties at room temperature (RT) and liquid nitrogen temperature (LNT) were investigated. Interfacial characteristics of the nanocomposites were revealed through experimental and molecular dynamics (MD) simulation methods. It was found that m-XDA grafted GO (MAGO) showed better dispersion in the matrix and prominently higher efficiency in enhancing the mechanical properties of epoxy resin than D230 grafted GO (DAGO). MAGO nanocomposites exhibited tensile strength 18.1% and 11.3% higher than neat epoxy at RT and LNT, respectively. The result was highly consistent with the enhanced interfacial interaction energy between MAGO and epoxy compared to that between DAGO and epoxy as revealed by MD simulation. However, nanocomposites modified by AGO with improved amine grafting density didn't show enhanced mechanical properties as expected from MD simulation.
KW - Epoxy nanocomposites
KW - Graphene oxide
KW - Interfacial characteristics
KW - Mechanical properties
KW - Surface functionalization
UR - https://www.scopus.com/pages/publications/85107143572
U2 - 10.1016/j.apsusc.2021.149964
DO - 10.1016/j.apsusc.2021.149964
M3 - 文章
AN - SCOPUS:85107143572
SN - 0169-4332
VL - 558
JO - Applied Surface Science
JF - Applied Surface Science
M1 - 149964
ER -