Electromagnetic and microwave absorption properties of Fe₃O₄ magnetic films plated on hollow glass spheres

Magnetic hollow spheres of low density were prepared by plating Fe₃O₄ magnetic films on hollow glass spheres using ferrite plating. The complex permeability and permittivity of spheres-wax composites were measured in the range of 2-18 GHz. The complex permeability and permittivity increased, and the dielectric and magnetic losses were improved as the volume fraction of the magnetic spheres in the composites increased from 60% to 80%, which also resulted in a great improvement of microwave absorption properties. For composites with volume fraction 80%, its magnetic resonance frequency was at about 13 GHz and it appeared three loss peaks in the calculated reflection loss curves; the bandwidth less than -10 dB was almost 4 GHz which was just in the Ku-band frequencies (12-18 GHz) and a minimum reflection loss of -20 dB was obtained when the thickness was 2.6 mm; the microwave absorbing properties were mainly due to the magnetic loss. The results showed that the magnetic spheres composites were good and light microwave absorbers in the Ku-band frequencies.