Effect of solution and aging temperatures on microstructure and mechanical properties of 10Cr13Co13Mo5Ni3W1VE(S280) steel

The article investigated the effects of solution and ging temperatures on microstructure and mechanical properties of ultra-high strength stainless steel 10Cr13Co13Mo5Ni3W1VE(S280). Higher solution temperatures can improve impact toughness because of the quantity reduction of submicron-sized particles which act as microporous nucleation sites. S280 has the best mechanical properties at 1080 °C solution temperature. After quenching, the steel is completely martensite with almost no retained austenite. Aging at 560 °C results in peak strength due to the precipitation of fine carbides coherent zones. The loss of precipitates/matrix coherency and precipitates coarsening cause a decrease in strength at higher aging temperatures. Good strength and toughness obtained at 540 °C aging temperature are attributed to fine and dispersed strengthening phases such as Cr₂C and Fe₂Mo, and the recovery of austenite in high-density dislocation martensite matrix. The details of electron microscopy research, strengthening and toughening mechanisms are discussed.