Effect of chromium substitution on structure and magnetic properties of Bi₂Fe₄O₉

Orthorhombic Bi₂Fe_{4 - x}Cr_xO₉ (x = 0.0, 0.25, and 0.75) nanoplatelets were synthesized by a simple hydrothermal method. The structure, morphology, and magnetic properties of the obtained powders have been characterized. Calculation of the lattice parameters of Bi₂Fe_{4 - x}Cr_xO₉, as well as bond lengths and angles, was carried out by X-ray diffraction Rietveld refinement. The volumes of the metal-oxygen tetrahedra and octahedra were calculated to be sequentially increasing as the Cr doping level increases. The samples undergo an antiferromagnetic transition at 250 ± 5 K. The magnetic moments of the samples increase with higher Cr doping level. The 3d electron spin state for Fe³⁺ in the as-prepared samples is different, which is possibly due to the distortion of Fe-O tetrahedra and octahedra in the crystal structure after chromium substitution.