Cyclic oxidation behavior of Al-Cu-Fe-Cr quasicrystalline coating on titanium alloy

Chungen Zhou; Fei Cai; Huibin Xu; Shengkai Gong

doi:10.1016/j.msea.2004.08.026

Cyclic oxidation behavior of Al-Cu-Fe-Cr quasicrystalline coating on titanium alloy

Chungen Zhou^*
, Fei Cai
, Huibin Xu
, Shengkai Gong

^*此作品的通讯作者

材料科学与工程学院

Beihang University

科研成果: 期刊稿件 › 文章 › 同行评审

15 引用（Scopus）

摘要

The Al-Cu-Fe-Cr quasicrystalline coating was deposited by low pressure plasma spraying (LPPS). Formation of Al-Cu-Fe-Cr quasicrystalline phase is closely related to annealing temperature. As-deposited Al-Cu-Fe-Cr coating is a kind of mixtures of quasicrystalline and crystalline phases. With increasing heat treatment temperature, icosahedral phase initially is increased and then decreased, the amount of crystalline phases is decreased and the amount of decagonal quasicrystalline phase is increased. Al-Cu-Fe-Cr quasicrystalline coating improved the cyclic oxidation resistance of titanium-based alloys. The weight gains at 650 and 800 °C for Al-Cu-Fe-Cr quasicrystalline coating are very low. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe-Cr quasicrystalline coating after oxidation consisted of Al₂O₃.

源语言	英语
页（从-至）	362-366
页数	5
期刊	Materials Science and Engineering: A
卷	386
期	1-2
DOI	https://doi.org/10.1016/j.msea.2004.08.026
出版状态	已出版 - 25 11月 2004

访问文件

10.1016/j.msea.2004.08.026

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{d93e49d31f204179942f3589b1c55dc1,

title = "Cyclic oxidation behavior of Al-Cu-Fe-Cr quasicrystalline coating on titanium alloy",

abstract = "The Al-Cu-Fe-Cr quasicrystalline coating was deposited by low pressure plasma spraying (LPPS). Formation of Al-Cu-Fe-Cr quasicrystalline phase is closely related to annealing temperature. As-deposited Al-Cu-Fe-Cr coating is a kind of mixtures of quasicrystalline and crystalline phases. With increasing heat treatment temperature, icosahedral phase initially is increased and then decreased, the amount of crystalline phases is decreased and the amount of decagonal quasicrystalline phase is increased. Al-Cu-Fe-Cr quasicrystalline coating improved the cyclic oxidation resistance of titanium-based alloys. The weight gains at 650 and 800 °C for Al-Cu-Fe-Cr quasicrystalline coating are very low. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe-Cr quasicrystalline coating after oxidation consisted of Al2O3.",

keywords = "Cyclic oxidation, Low pressure plasma spraying, Quasicrystal, Titanium alloy",

author = "Chungen Zhou and Fei Cai and Huibin Xu and Shengkai Gong",

year = "2004",

month = nov,

day = "25",

doi = "10.1016/j.msea.2004.08.026",

language = "英语",

volume = "386",

pages = "362--366",

journal = "Materials Science and Engineering: A",

issn = "0921-5093",

publisher = "Elsevier Ltd",

number = "1-2",

}

TY - JOUR

T1 - Cyclic oxidation behavior of Al-Cu-Fe-Cr quasicrystalline coating on titanium alloy

AU - Zhou, Chungen

AU - Cai, Fei

AU - Xu, Huibin

AU - Gong, Shengkai

PY - 2004/11/25

Y1 - 2004/11/25

N2 - The Al-Cu-Fe-Cr quasicrystalline coating was deposited by low pressure plasma spraying (LPPS). Formation of Al-Cu-Fe-Cr quasicrystalline phase is closely related to annealing temperature. As-deposited Al-Cu-Fe-Cr coating is a kind of mixtures of quasicrystalline and crystalline phases. With increasing heat treatment temperature, icosahedral phase initially is increased and then decreased, the amount of crystalline phases is decreased and the amount of decagonal quasicrystalline phase is increased. Al-Cu-Fe-Cr quasicrystalline coating improved the cyclic oxidation resistance of titanium-based alloys. The weight gains at 650 and 800 °C for Al-Cu-Fe-Cr quasicrystalline coating are very low. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe-Cr quasicrystalline coating after oxidation consisted of Al2O3.

AB - The Al-Cu-Fe-Cr quasicrystalline coating was deposited by low pressure plasma spraying (LPPS). Formation of Al-Cu-Fe-Cr quasicrystalline phase is closely related to annealing temperature. As-deposited Al-Cu-Fe-Cr coating is a kind of mixtures of quasicrystalline and crystalline phases. With increasing heat treatment temperature, icosahedral phase initially is increased and then decreased, the amount of crystalline phases is decreased and the amount of decagonal quasicrystalline phase is increased. Al-Cu-Fe-Cr quasicrystalline coating improved the cyclic oxidation resistance of titanium-based alloys. The weight gains at 650 and 800 °C for Al-Cu-Fe-Cr quasicrystalline coating are very low. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe-Cr quasicrystalline coating after oxidation consisted of Al2O3.

KW - Cyclic oxidation

KW - Low pressure plasma spraying

KW - Quasicrystal

KW - Titanium alloy

UR - https://www.scopus.com/pages/publications/6344285846

U2 - 10.1016/j.msea.2004.08.026

DO - 10.1016/j.msea.2004.08.026

M3 - 文章

AN - SCOPUS:6344285846

SN - 0921-5093

VL - 386

SP - 362

EP - 366

JO - Materials Science and Engineering: A

JF - Materials Science and Engineering: A

IS - 1-2

ER -

Cyclic oxidation behavior of Al-Cu-Fe-Cr quasicrystalline coating on titanium alloy

摘要

访问文件

其它文件与链接

指纹

引用此