Corrigendum to ‘Characterization and formation mechanism of ultra-fine ferrite grains in dissimilar metal weld between austenitic stainless steel and low alloy ferritic steel’ [Mater. Charact. https://doi.org/10.1016/j.matchar.2020.110777] (Materials Characterization (2021) 171, (S1044580320322488), (10.1016/j.matchar.2020.110777))

The authors regret in section 2.1 “Shielded metal arc welding with Inconel 182 electrode (ENiCrFe-3) was used for filling passes” should be “Tungsten inert gas welding with Inconel 82 (ERNiCr-3) filler wire was used for filling passes”, and “The chemical composition (wt%) of filler metal is 13.0–17.0 Cr, 0.10C, ≥59.0 Ni, 10.0 Fe, 5.0–9.0 Mn, 1.0 Nb, 1.0 Ti, 1.0 Si, 0.015 S, 0.03 P and ≤ 0.5 Cu” should be “The chemical composition (wt%) of filler metal is 18.0–22.0 Cr, 0.10 C, ≥67.0 Ni, 3.0 Fe, 2.5–3.5 Mn, 1.0–3.0 Nb, ≤ 0.75 Ti, ≤ 0.5 Cu, ≤ 0.12 Co, 0.5 Si, 0.015 S and 0.03 P". The authors would like to apologise for any inconvenience caused.