Atmospheric corrosion of field-exposed AZ31 magnesium in a tropical marine environment

Zhongyu Cui; Xiaogang Li; Kui Xiao; Chaofang Dong

doi:10.1016/j.corsci.2013.06.047

Atmospheric corrosion of field-exposed AZ31 magnesium in a tropical marine environment

Zhongyu Cui
, Xiaogang Li^*
, Kui Xiao
, Chaofang Dong

^*此作品的通讯作者

University of Science and Technology Beijing

科研成果: 期刊稿件 › 文章 › 同行评审

187 引用（Scopus）

摘要

Corrosion behavior of AZ31 magnesium in tropical marine atmosphere was investigated. Chloride ions deposition rate played an important role in the corrosion process, which resulted in an obvious fluctuation of the corrosion rate. The corrosion was initiated from pitting corrosion and then evolved into general corrosion as the exposure time extended. Mg₅(CO₃)₄(OH)₂·xH₂O was the dominate products during the whole exposure periods. The products on the specimens weathered for 1, 6 and 12months slightly suppressed the corrosion process, while that generated after 24months of exposure exhibited good protective ability against further corrosion attacks.

源语言	英语
页（从-至）	243-256
页数	14
期刊	Corrosion Science
卷	76
DOI	https://doi.org/10.1016/j.corsci.2013.06.047
出版状态	已出版 - 11月 2013
已对外发布	是

联合国可持续发展目标

此成果有助于实现下列可持续发展目标：

可持续发展目标 14 水下生物

访问文件

10.1016/j.corsci.2013.06.047

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{e0d0186194db465e871cbdbe96de1901,

title = "Atmospheric corrosion of field-exposed AZ31 magnesium in a tropical marine environment",

abstract = "Corrosion behavior of AZ31 magnesium in tropical marine atmosphere was investigated. Chloride ions deposition rate played an important role in the corrosion process, which resulted in an obvious fluctuation of the corrosion rate. The corrosion was initiated from pitting corrosion and then evolved into general corrosion as the exposure time extended. Mg5(CO3)4(OH)2·xH2O was the dominate products during the whole exposure periods. The products on the specimens weathered for 1, 6 and 12months slightly suppressed the corrosion process, while that generated after 24months of exposure exhibited good protective ability against further corrosion attacks.",

keywords = "A. Magnesium, B. EIS, C. Atmospheric corrosion, C. Pitting corrosion, C. Rust",

author = "Zhongyu Cui and Xiaogang Li and Kui Xiao and Chaofang Dong",

year = "2013",

month = nov,

doi = "10.1016/j.corsci.2013.06.047",

language = "英语",

volume = "76",

pages = "243--256",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Atmospheric corrosion of field-exposed AZ31 magnesium in a tropical marine environment

AU - Cui, Zhongyu

AU - Li, Xiaogang

AU - Xiao, Kui

AU - Dong, Chaofang

PY - 2013/11

Y1 - 2013/11

N2 - Corrosion behavior of AZ31 magnesium in tropical marine atmosphere was investigated. Chloride ions deposition rate played an important role in the corrosion process, which resulted in an obvious fluctuation of the corrosion rate. The corrosion was initiated from pitting corrosion and then evolved into general corrosion as the exposure time extended. Mg5(CO3)4(OH)2·xH2O was the dominate products during the whole exposure periods. The products on the specimens weathered for 1, 6 and 12months slightly suppressed the corrosion process, while that generated after 24months of exposure exhibited good protective ability against further corrosion attacks.

AB - Corrosion behavior of AZ31 magnesium in tropical marine atmosphere was investigated. Chloride ions deposition rate played an important role in the corrosion process, which resulted in an obvious fluctuation of the corrosion rate. The corrosion was initiated from pitting corrosion and then evolved into general corrosion as the exposure time extended. Mg5(CO3)4(OH)2·xH2O was the dominate products during the whole exposure periods. The products on the specimens weathered for 1, 6 and 12months slightly suppressed the corrosion process, while that generated after 24months of exposure exhibited good protective ability against further corrosion attacks.

KW - A. Magnesium

KW - B. EIS

KW - C. Atmospheric corrosion

KW - C. Pitting corrosion

KW - C. Rust

UR - https://www.scopus.com/pages/publications/84883231889

U2 - 10.1016/j.corsci.2013.06.047

DO - 10.1016/j.corsci.2013.06.047

M3 - 文章

AN - SCOPUS:84883231889

SN - 0010-938X

VL - 76

SP - 243

EP - 256

JO - Corrosion Science

JF - Corrosion Science

ER -

Atmospheric corrosion of field-exposed AZ31 magnesium in a tropical marine environment

摘要

联合国可持续发展目标

访问文件

其它文件与链接

学术指纹

引用此