A Finite Element and Experimental Analysis of Composite T-Joints Used in Wind Turbine Blades

In this study, a finite element failure model was created using ABAQUS to determine the location where delamination is initiated and its subsequent propagation. The effect of fibre-reinforced structures on delamination behaviour was studied. The composite T-joints were made of glass fabric infused with epoxy resin using a vacuum assisted resin transfer moulding technique. The veil layer and 3D weave techniques were employed to improve the properties in the through-thickness direction that can delay or prevent delamination when in service. All the pull-out tensile tests were conducted in an Instron testing machine using a specially designed test fixture. The 3D weave T-joints were found to have improved performance under both static and fatigue loading. Increasing the static properties increases fatigue life performance. The location for the through-thickness reinforcement plays an important role in extending fatigue life of the T-joints.