Solvent Engineering Boosts the Efficiency of Paintable Carbon-Based Perovskite Solar Cells to beyond 14%

Carbon-based hole transport material (HTM)-free perovskite solar cells (PSCs) have shown much promise for practical applications because of their high stability and low cost. However, the efficiencies of this kind of PSCs are still relatively low, especially for the simplest paintable carbon-based PSCs, in comparison with the organic HTM-based PSCs. This can be imputed to the perovskite deposition methods that are not very suitable for this kind of devices. A solvent engineering strategy based on two-step sequential method is exploited to prepare a high-quality perovskite layer for the paintable carbon-based PSCs in which the solvent for CH₃NH₃I (MAI) solution at the second step is changed from isopropanol (IPA) to a mixed solvent of IPA/Cyclohexane (CYHEX). This mixed solvent not only accelerates the conversion of PbI₂ to CH₃NH₃PbI₃ but also suppresses the Ostwald ripening process resulting in a high-quality perovskite layer, e.g., pure phase, even surface, and compact capping layer. The paintable carbon-based PSCs fabricated from IPA/CYHEX solvent exhibits a considerable enhancement in photovoltaic performance and performance reproducibility in comparison with that from pure IPA, especially on fill factor (FF), owing mainly to the better contact of perovskite/carbon interface, lower trap density in perovskite, higher light absorption ability, and faster charge transport of perovskite layer. As a result, the highest power conversion efficiency (PCE) of 14.38% is obtained, which is a record value for carbon-based HTM-free PSCs. Furthermore, a PCE of as high as 10% is achieved for the large area device (1 cm²), also the highest of its kind.