Simple sol-gel route to synthesis of mesoporous TiO2

Xin Zhang; Xiaogang Li; Junsheng Wu; Renchun Yang; Limin Tian; Zhihua Zhang

doi:10.1007/s10971-009-1984-4

Simple sol-gel route to synthesis of mesoporous TiO₂

Xin Zhang
, Xiaogang Li^*
, Junsheng Wu
, Renchun Yang
, Limin Tian
, Zhihua Zhang

^*Corresponding author for this work

University of Science and Technology Beijing
China National Petroleum Corporation

Research output: Contribution to journal › Article › peer-review

9 Scopus citations

Abstract

Mesoporous TiO₂ with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO₂ had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m² g^-1 after calcinating at 450 °C.

Original language	English
Pages (from-to)	1-3
Number of pages	3
Journal	Journal of Sol-Gel Science and Technology
Volume	51
Issue number	1
DOIs	https://doi.org/10.1007/s10971-009-1984-4
State	Published - Jul 2009
Externally published	Yes

Keywords

Formamide
Mesoporous TiO
Sol-gel
Titanium sulfate

Access to Document

10.1007/s10971-009-1984-4

Cite this

@article{a0ee83fe9b36401f9aa6f5e3350311d9,

title = "Simple sol-gel route to synthesis of mesoporous TiO2",

abstract = "Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.",

keywords = "Formamide, Mesoporous TiO, Sol-gel, Titanium sulfate",

author = "Xin Zhang and Xiaogang Li and Junsheng Wu and Renchun Yang and Limin Tian and Zhihua Zhang",

year = "2009",

month = jul,

doi = "10.1007/s10971-009-1984-4",

language = "英语",

volume = "51",

pages = "1--3",

journal = "Journal of Sol-Gel Science and Technology",

issn = "0928-0707",

publisher = "Springer Netherlands",

number = "1",

}

TY - JOUR

T1 - Simple sol-gel route to synthesis of mesoporous TiO2

AU - Zhang, Xin

AU - Li, Xiaogang

AU - Wu, Junsheng

AU - Yang, Renchun

AU - Tian, Limin

AU - Zhang, Zhihua

PY - 2009/7

Y1 - 2009/7

N2 - Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.

AB - Mesoporous TiO2 with a high specific surface area was prepared from titanium sulfate solution in a simple sol-gel route, where formamide was used as pH adjusting agent. TiO2 had a high resistance to phase transformation, and maintained monophasic anatase after calcinating at 600 °C. The highest specific surface area achieved on the prepared samples is 231.90 m2 g-1 after calcinating at 450 °C.

KW - Formamide

KW - Mesoporous TiO

KW - Sol-gel

KW - Titanium sulfate

UR - https://www.scopus.com/pages/publications/65649120034

U2 - 10.1007/s10971-009-1984-4

DO - 10.1007/s10971-009-1984-4

M3 - 文章

AN - SCOPUS:65649120034

SN - 0928-0707

VL - 51

SP - 1

EP - 3

JO - Journal of Sol-Gel Science and Technology

JF - Journal of Sol-Gel Science and Technology

IS - 1

ER -

Simple sol-gel route to synthesis of mesoporous TiO₂

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this