@inproceedings{e83b2dde216640e38fe5120a1116a1e6,
title = "Preparation of calcium silicate board by fly-ash based calcium silicate powder by press molding",
abstract = "Calcium silicate board has been prepared by press molding from fly-ash based calcium silicate powder with the pulp fiber as the reinforcing fibre. The micro-morphology and crystal structure of the obtained calcium silicate board were analyzed by SEM and XRD. The effects of cement,silica fume and molding pressure on the flexural strength and thermal conductivity of calcium silicate board were investigated. When the molding pressure is 10MPa, samples' flexural strength, bulk density and thermal conductivity are 5MPa, 0.7g/cm3 and 0.12 W/m·K respectively. It was found that this kind of calcium silicate powder was complete hydrated and could not be further hydrated even in autoclave curing.",
keywords = "Calcium silicate board, Enhance fiber, Press molding",
author = "Shuli Wang and Guotong Qin and Wei Wei",
year = "2013",
doi = "10.4028/www.scientific.net/MSF.743-744.603",
language = "英语",
isbn = "9783037856062",
series = "Materials Science Forum",
publisher = "Trans Tech Publications Ltd",
pages = "603--606",
editor = "Xinfeng Tang and Ying Wu and Yan Yao and Zengzhi Zhang and Zengzhi Zhang",
booktitle = "Energy and Environment Materials",
address = "瑞士",
note = "Chinese Materials Congress 2012, CMC 2012 ; Conference date: 13-07-2012 Through 18-07-2012",
}