Polymorphic transformation and magnetic properties of rapidly solidified Fe _26.7 Co _26.7 Ni _26.7 Si _8.9 B _11.0 high-entropy alloys

In this work, the microstructural evolution and magnetic performance of the melt-spun amorphous and amorphous-crystalline Fe _26.7 Co _26.7 Ni _26.7 Si _8.9 B _11.0 high-entropy alloys (HEAs) during crystallization were investigated, respectively. Upon heating fully amorphous ribbons, a metastable BCC supersaturated solid solution together with a little Ni ₃₁ Si ₁₂ crystals first precipitated and then the (Fe,Co) ₂ B crystals formed until the full crystallization was achieved. With further increasing temperature after full crystallization, a polymorphic transformation from a metastable BCC phase to two types of FCC solid solutions occurred. For the amorphous-crystalline HEAs, the dominant crystallization products were the metastable FCC but not BCC crystals. During crystallization, the primary metastable FCC crystals first transform into the metastable BCC crystals and then the newly-generated BCC phase transforms into two types of FCC phases with further increasing temperature. This temperature dependence of the gradual polymorphic transformation results in the change of magnetic properties of the present high-entropy amorphous alloys.