Optimized Ti-O Subcompounds and Elastic Expanded MXene Interlayers Boost Quick Sodium Storage Performance

To develop quick-charge sodium-ion battery, it is significant to optimize insertion-type anode to afford fast Na⁺ diffusion rate and excellent electron conductivity. First-principles calculations reveal the Ti-O subcompound superiority for Na⁺ diffusion following Ti(II)-O > Ti(III)-O > Ti(IV)-O. Hence, in situ growth of amorphous Ti-O subcompounds with rich oxygen defects based on Ti₃C₂T_x-MXene is developed. Meanwhile, the composite presents expanded MXene interlayer spacing and much enhanced conductivity. The synergistic effect of enhanced electron/ion conduction gives a high capacity of 107 mAh g⁻¹ at 50 A g⁻¹, which gives 50% and 150% increasements compared with one counterpart without valence adjustment and another one without MXene expansion. It only needs 20 s (at 30 A g⁻¹) to complete the discharge/charge process and obtains a capacity of 144.5 mAh g⁻¹, which also shows a long-term cycling stability at quick-charge mode (121 mAh g⁻¹ after 10000 cycles at 10 A g⁻¹). The enhanced performance comes from fast electron transfer among Ti-O subcompounds contributed by rich-defect amorphous TiO_2–x, and a reversible change of elastic MXene with interlayer spacing between 1.4 and 1.9 nm during Na⁺ insertion/extraction process. This study provides a feasible route to boost the kinetics and develop quick-charge sodium-ion battery.