Hot Deformation Behavior and Microstructure Evolution of a Fe-Ni-Cr Based Superalloy

The present study systematically investigated the hot deformation behavior of GH2787 superalloy within the temperature range of 1060–1120 °C and strain rates of 0.1–10 s⁻¹. An Arrhenius-type constitutive equation was developed that accurately predicts the flow behavior, and the calculated thermal deformation activation energy Q is 364,401.19 J/mol. The hot working map was constructed based on the dynamic material model, which identified two preferred processing regions with power dissipation efficiency exceeding 0.3, and no flow instability was observed across the entire parameter range. Microstructural analysis reveals that the extent of dynamic recrystallization significantly increases with rising temperature and strain rate. Discontinuous dynamic recrystallization (via grain boundary bulging nucleation) serves as the dominant recrystallization mechanism in GH2787 superalloy during hot deformation, while continuous dynamic recrystallization (via subgrain rotation and coalescence) acts as a synergistic auxiliary mechanism, jointly driving microstructural evolution. This study provides important theoretical foundations for optimizing the hot working processes of GH2787 superalloy.