Enhancement the armor shielding properties of cf/epoxy composite by addition nanoparticles of magnetic iron oxide

In the present investigation, we prepared two types of CF composites. The first prepared composite sample was CF/epoxy resin composite and the second was CF/epoxy resin / with a different weight ratio of magnetic iron oxide. Magnetic iron oxide was prepared by co-precipitation method, with particle sizes measured in range 25:35 nm. The resistance to penetration of high kinetic energy projectile of the prepared composite sample was measured and It was found that addition of 5% nano-particles of magnetic iron oxide to composite material sample decrease the residual velocity of projectile penetrating it by 9%.i.e increasing resistance of the sample to penetration of high kinetic energy projectile.it was found that the Resistance to penetration of sheet of composite material sampleC4 of weight=40.32kg to projectile 7.62×39 mm AP at distance 15m equivalent to resistance of steel sheet of weight =54.6 kg at distance 200m.Resistance to penetration of sheet of composite material sampleC4 to projectile 7.62×39 mm AP at distance 10m equivalent to the resistance of high-quality steel sheet(steel4340) of weight=47.85 kg at distance 25m.