Electrical and Thermal Transport Properties of Ge_1–xPb_xCu_ySb_yTeSe_2y

Balancing the contradictory relationship between thermoelectric parameters, such as effective mass and carrier mobility, is a challenge to optimize thermoelectric performance. Herein, the exceptional thermoelectric performance is realized in GeTe through collaboratively optimizing the carrier and phonon transport via stepwise alloying Pb and CuSbSe₂. The formation energy of Ge vacancy is efficiently bolstered by alloying Pb, which reduces carrier density and carrier scattering to maintain superior carrier mobility in GeTe. Additionally, CuSbSe₂, acting as an n-type dopant, further modulates carrier density and validly equilibrates carrier mobility and effective mass. Accordingly, the promising power factor of 45 µW cm⁻¹ K⁻² is achieved at 723 K. Meanwhile, point defects are found to significantly suppress phonons transport to descend lattice thermal conductivity by Pb and CuSbSe₂ alloying, which barely impacts the carrier mobility. A combination with superior carrier mobility and lower lattice thermal conductivity, a maximum ZT of 2.2 is attained in Ge_0.925Pb_0.075Cu_0.005Sb_0.005TeSe_0.01, which corresponds to a 100% promotion compared with that of intrinsic GeTe. This study provides a new indicator for optimizing carrier and phonon transport properties by balancing interrelated thermoelectric parameters.