Effect of SiC nanowires on the mechanical properties and thermal conductivity of 3D-SiC_f/SiC composites prepared via precursor infiltration pyrolysis

In this study, SiC nanowires (SiC_NWS) were grown in situ on the surface of PyC interface through chemical vapor infiltration (CVI) to improve the mechanical characteristics and thermal conductivity of three-dimensional SiC_f/SiC composites fabricated via precursor infiltration pyrolysis (PIP). The effect of SiC_NWS on the properties of the obtained composites was investigated by comparing them with conventional SiC_f/PyC/SiC composites. After the deposition of SiC_NWS, the flexural strength of the SiC_f/SiC composites was found to increase by 46 %, and the thermal conductivity showed an obvious increase at 25−1000 °C. The energy release of the composites in the damage evolution process was analysed by acoustic emission. The results indicated that the damage evolution process was delayed owing to the decrease in porosity, the crack deflection and bridging of the SiC_NWS. Furthermore, the excellent thermal conductivity was attributed to the thermally conductive pathways formed by the SiC_NWS in the dense structure.