Carbon quantum dot regulated electrochemical activation of Co_0.03Ni_0.97LDH for energy storage

The valence and coordination structure of transition metals in electrode materials play a crucial role in the electrochemical energy storage process. However, it is still challenging to modulate the chemical environment of transition metals in multi-metal-based electrode materials because of the presence of charge exchange between the different metal ions. Here, a bimetallic-based electrode material, Co_0.03Ni_0.97LDH, with low electrochemical activity is transformed into a highly active one through a simple and efficient electrochemical activation process with the assistance of carbon quantum dots (CQDs). It reveals that CQDs can provide a fast charge transfer channel for the unique valence regulation between Co and Ni, resulting in the generation of high concentrations of Co³⁺ and Ni²⁺, which is beneficial for upgrading the energy density of the electrode material and mitigating the Jahn-Teller distortion during the conversion of Ni²⁺/Ni³⁺. Moreover, the distinctive 5-coordination structures of Co can effectively stabilize the active sites of both Ni²⁺ and Co³⁺. The activated CQD-modified Co_0.03Ni_0.97LDH composites (A-CQD/Co_0.03Ni_0.97LDH) deliver a high specific capacity of 2408 F g⁻¹ at 1 A g⁻¹ and maintain a high capacity retention of 90% after 2000 cycles at 10 A g⁻¹. The assembled asymmetric supercapacitor and the aqueous Ni-Zn battery show a high energy storage density of 0.25 mW h cm⁻² at a power density of 2.25 mW cm⁻² and 1.44 mW h cm⁻² at 0.72 mW cm⁻², respectively. The impressive results provide a feasible strategy for the rational design of multi-metal-based electrode materials.